# Hydrogen embrittlement of steels: trap the hydrogen before it finds the crack

> A tensile specimen cut open to its grains and read as the path of one hydrogen atom: H₂ splits at the surface, the atoms hop between tetrahedral sites of the iron lattice, defects hold some back, fine carbides lock them away and, where hydrogen gets through, a crack opens. Five cards explain each station, from the sources of hydrogen to the two mechanisms (HEDE and HELP) and the designed traps that make steels more resistant.

- Page: https://www.labcanvas.com/templates/graphical-abstracts/hydrogen-embrittlement-steels-trap-hydrogen-before-it-finds-crack
- Open in the LabCanvas editor (LabCanvas account): https://www.labcanvas.com/editor.html?template=hydrogen-embrittlement-of-steels-trap-the-hydrogen
- Updated: 2026-10-14
- Category: Graphical abstracts
- Method: Graphical abstract
- Starting materials: Hydrogen from gas, electrochemical charging or corrosion
- Product: A steel whose designed traps keep hydrogen away from crack-prone sites
- Key result: Diffusion barrier 0.088 eV in iron; diffusivity in α-Fe up to 10⁵ × that in Ni; irreversible traps > 60 kJ/mol; pipeline steel: strength −50 %, ductility −90 % (Yu et al. 2024); κ-carbides 2–4 nm (Xiong et al. 2024); ×2 HE resistance (Sun et al. 2021)
- Figure: 1920 × 1080 px, 306 editable layers (3 generated objects with settings)

## Steps

1. **Entry**: H₂ dissociates into atoms at the surface, probably the rate-limiting step of entry (H–H bond about 4.48 eV, lowered at a surface); gas, electrochemical reactions and corrosion all supply hydrogen (Yu et al. 2024; Shulin et al. 2026)
2. **Diffusion**: In iron, H sits in tetrahedral interstitial sites and hops between them over a barrier of 0.088 eV; its diffusivity in α-Fe can be five orders of magnitude higher than in nickel (Yu et al. 2024)
3. **Trapping**: Vacancies, dislocations, grain boundaries and phase boundaries trap H reversibly; carbides and microvoids trap it irreversibly (binding energy > 60 kJ/mol); deeper traps release H at higher temperature in thermal desorption (Yu et al. 2024)
4. **Designed traps**: Atom probe shows H inside fine V–Mo–Nb carbides (Chen et al. 2017) and at incoherent NbC interfaces, dislocations and grain boundaries (Chen et al. 2020); 2–4 nm κ-carbides mitigate embrittlement, coarse grain-boundary carbides worsen it (Xiong et al. 2024)
5. **Embrittlement**: HEDE (weakened lattice and interfaces) and HELP (more mobile dislocations) act together; H cut a pipeline steel’s strength by over 50 % and its ductility by over 90 % (Yu et al. 2024); Mn-rich zones that arrest microcracks doubled HE resistance (Sun et al. 2021)

## Uses

- Graphical abstracts on hydrogen embrittlement and hydrogen-compatible steels
- Talks on pipelines, tanks and materials for the hydrogen economy
- Teaching hydrogen diffusion and trapping in metals

## References

1. Yu et al., “Hydrogen Embrittlement as a Conspicuous Material Challenge─Comprehensive Review and Future Directions”, Chemical Reviews 2024. https://doi.org/10.1021/acs.chemrev.3c00624 (review)
2. Chen et al., “Direct observation of individual hydrogen atoms at trapping sites in a ferritic steel”, Science 2017. https://doi.org/10.1126/science.aal2418 (primary)
3. Chen et al., “Observation of hydrogen trapping at dislocations, grain boundaries, and precipitates”, Science 2020. https://doi.org/10.1126/science.aaz0122 (primary)
4. Sun et al., “Chemical heterogeneity enhances hydrogen resistance in high-strength steels”, Nature Materials 2021. https://doi.org/10.1038/s41563-021-01050-y (primary)
5. Xiong et al., “Impact of Size and Distribution of k-Carbides on the Hydrogen Embrittlement and Trapping Behaviors of a Fe-Mn-Al-C Low-Density Steel”, Materials 2024. https://doi.org/10.3390/ma17112698 (primary)
6. Shulin et al., “Mechanisms of hydrogen embrittlement, mitigation strategies, and emerging materials for hydrogen energy and advanced manufacturing”, Frontiers in Chemistry 2026. https://doi.org/10.3389/fchem.2026.1957974 (further reading)

Credit: Drawn by LabCanvas after Yu et al., Chem. Rev. 2024 (doi:10.1021/acs.chemrev.3c00624); Chen et al., Science 2017 (doi:10.1126/science.aal2418) and 2020 (doi:10.1126/science.aaz0122); Sun et al., Nat. Mater. 2021 (doi:10.1038/s41563-021-01050-y) and Xiong et al., Materials 2024 (doi:10.3390/ma17112698).

## Questions

**What does the “Hydrogen embrittlement of steels: trap the hydrogen before it finds the crack” template show?** A tensile specimen cut open to its grains and read as the path of one hydrogen atom: H₂ splits at the surface, the atoms hop between tetrahedral sites of the iron lattice, defects hold some back, fine carbides lock them away and, where hydrogen gets through, a crack opens. Five cards explain each station, from the sources of hydrogen to the two mechanisms (HEDE and HELP) and the designed traps that make steels more resistant.

**What are the steps shown in “Hydrogen embrittlement of steels: trap the hydrogen before it finds the crack”?** 1. Entry: H₂ dissociates into atoms at the surface, probably the rate-limiting step of entry (H–H bond about 4.48 eV, lowered at a surface); gas, electrochemical reactions and corrosion all supply hydrogen (Yu et al. 2024; Shulin et al. 2026). 2. Diffusion: In iron, H sits in tetrahedral interstitial sites and hops between them over a barrier of 0.088 eV; its diffusivity in α-Fe can be five orders of magnitude higher than in nickel (Yu et al. 2024). 3. Trapping: Vacancies, dislocations, grain boundaries and phase boundaries trap H reversibly; carbides and microvoids trap it irreversibly (binding energy > 60 kJ/mol); deeper traps release H at higher temperature in thermal desorption (Yu et al. 2024). 4. Designed traps: Atom probe shows H inside fine V–Mo–Nb carbides (Chen et al. 2017) and at incoherent NbC interfaces, dislocations and grain boundaries (Chen et al. 2020); 2–4 nm κ-carbides mitigate embrittlement, coarse grain-boundary carbides worsen it (Xiong et al. 2024). 5. Embrittlement: HEDE (weakened lattice and interfaces) and HELP (more mobile dislocations) act together; H cut a pipeline steel’s strength by over 50 % and its ductility by over 90 % (Yu et al. 2024); Mn-rich zones that arrest microcracks doubled HE resistance (Sun et al. 2021).

**What are the starting materials and the product?** Starting materials: Hydrogen from gas, electrochemical charging or corrosion. Product: A steel whose designed traps keep hydrogen away from crack-prone sites.

**Which papers is “Hydrogen embrittlement of steels: trap the hydrogen before it finds the crack” based on?** Yu et al., “Hydrogen Embrittlement as a Conspicuous Material Challenge─Comprehensive Review and Future Directions”, Chemical Reviews 2024 (doi:10.1021/acs.chemrev.3c00624); Chen et al., “Direct observation of individual hydrogen atoms at trapping sites in a ferritic steel”, Science 2017 (doi:10.1126/science.aal2418); Chen et al., “Observation of hydrogen trapping at dislocations, grain boundaries, and precipitates”, Science 2020 (doi:10.1126/science.aaz0122); Sun et al., “Chemical heterogeneity enhances hydrogen resistance in high-strength steels”, Nature Materials 2021 (doi:10.1038/s41563-021-01050-y); Xiong et al., “Impact of Size and Distribution of k-Carbides on the Hydrogen Embrittlement and Trapping Behaviors of a Fe-Mn-Al-C Low-Density Steel”, Materials 2024 (doi:10.3390/ma17112698); Shulin et al., “Mechanisms of hydrogen embrittlement, mitigation strategies, and emerging materials for hydrogen energy and advanced manufacturing”, Frontiers in Chemistry 2026 (doi:10.3389/fchem.2026.1957974).

**Can I edit the “Hydrogen embrittlement of steels: trap the hydrogen before it finds the crack” template?** Yes. Open it in the LabCanvas editor: all 306 layers are editable, including 3 generated objects (structures, plots, equipment) with their own settings. Change the text, colours and layout, then export PNG, TIFF, SVG or PDF.

**Do I need an account to use this template?** Not to view it here. To open and edit it, sign in to LabCanvas or create a free account (the free plan keeps up to 3 designs). Downloading the figure is part of LabCanvas Pro (US$19 a month or US$199 a year).